PA 66GF30 FR is a Nylon 66 with 30% glass-fibers and flame retardant halogenated.
Typical Application of PA66 GF30 Halogenated FR (A2014F)
The advantage of nylon 66 GF30 halogenated FR can maintain the original physical and chemical properties of flame retardant products.
Processing Detail of pa66 fr 30 Halogenated FR (A2014F)
Other Details of PA66 GF30 Halogenated FR (A2014F)
Physical Property
|
Ash |
(30.0% 1 ISO3451/1) |
|
Conditioned |
600°C*2h |
|
Density |
(1590Kg/m3 1 ISO1183) |
|
Conditioned |
23°C |
|
Shrinkage Parallel Flow |
(0.2-0.5 % 1 ISO294-4) |
|
Shrinkage Vertical Flow |
(0.6-0.9% I ISO294-4) |
Mechanical Properties
|
Tensile strength (155.0MPa 1 ISO527) Conditioned |
5mm/ min |
|
Tensile Strain at Break (2.7% I ISO527) Conditioned |
5mm/min |
|
Notched Impact Strength (8.5 KJ/m2I ISO527) Conditioned |
1.0J |
|
Flexural Strength (240MPa 1ISO178) Conditioned |
2mm/min |
|
Flexural Modulus (10258 MPa I ISO178) Conditioned |
2mm/ min |
Thermal Property
|
Melting Point |
(260°C I ISO11357) |
|
Hot Deformation Temperature |
(245*C I ISO75) |
|
Conditioned |
1.8MPa |
|
Flammability Class |
(HB 1UL94) |
|
Conditioned |
1.6mm |
Injection Molding Conditions
|
Drying Temperature |
130°C |
|
Drying Time |
3h |
|
Cylinder Temperature |
280-300°C |
|
Nozzle Temperature |
280-300*C |
|
Tooling Temperature |
80-100*C |
* Molding conditions are just for reference, please make an adjustment based on the actual situation！