PA6 6GF15 is a 15% glass fiber reinforced, toughened, polyamide 66 resin for injection molding.
Typical Application of PA66 GF15 With High Tensile Strength (A2307C)
PA66 15% glass fiber and high toughness modified grades are applied to the sectors of electrical switch with high tensile characteristics.
Processing Detail of PA66 GF15 With High Tensile Strength (A2307C)
Other Details of PA66 GF15 With High Tensile Strength (A2307C)
|
Ash |
(15.0% 1 ISO3451/1) |
|
Conditioned |
600°C*2h |
|
Density |
(1180Kg/m3 1 ISO1183) |
|
Conditioned |
23°C |
|
Shrinkage Parallel Flow |
(0.7-1.0 % 1 ISO294-4) |
|
Shrinkage Vertical Flow |
(1.0-1.4% I ISO294-4) |
Mechanical Properties
|
Tensile strength (105.0MPa 1 ISO527) Conditioned |
5mm/ min |
|
Tensile Strain at Break (2.6% I ISO527) Conditioned |
5mm/min |
|
Notched Impact Strength (10.0 KJ/m2 I ISO179) Conditioned |
1.0J |
|
Flexural Strength (177MPa 1ISO178) Conditioned |
2mm/min |
|
Flexural Modulus (5050 MPa I ISO178) Conditioned |
2mm/min |
Thermal Property
|
Melting Point |
(260°C I ISO11357) |
|
Hot Deformation Temperature |
(225*C I ISO75) |
|
Conditioned |
1.8MPa |
|
Flammability Class |
(HB 1UL94) |
|
Conditioned |
mm |
Injection Molding Conditions
|
Drying Temperature |
130°C |
|
Drying Time |
3h |
|
Cylinder Temperature |
280-300°C |
|
Nozzle Temperature |
280-300*C |
|
Tooling Temperature |
80-100*C |
* Molding conditions are just for reference, please make an adjustment based on the actual situation！